Properties | Test Standards | Units | Typical Values | |
RL-SMC-3128 | RL-SMC-3002 | |||
Fibergalss Content | GB/T | wt% | 32 | 30 |
15568-2008 | ||||
Molding Temperature | ℃ | 135-155 | 135-155 | |
Molding Pressure | MPa | 20th Oct | 10th July | |
Shrinkage | % | 0.11±0.03 | -0.05±0.03 | |
Density | GB/T 1463-2005 | g/cm³ | 1.81±0.02 | 1.47±0.03 |
Tensile Strength | GB/T 1447-2005 | MPa | ≥80 | ≥65 |
Flexural Strength | GB/T 1449-2005 | MPa | ≥160 | ≥130 |
Flexural Modulus | GB/T 1449-2005 | GPa | ≥9 | ≥9 |
Impact Strength | GB/T 1451-2005 | kJ/㎡ | ≥70 | ≥60 |
Main Features | Good liquidity/ High strength | Low density/ Suitable for painting | ||
Application | Structure parts of rail transit | Light weight |