Fiberglass Stitched Fabric_Changzhou Rule Composite Material Co., Ltd,

Fiberglass Stitched Fabric

Fiberglass stitched fabric compatible with Polyester Vinyl and Epoxy resin and widely used in pultrusion pipes and tanks FRP boat insulation panels anode tubes auto parts bath tubes etc suitable for pultrusion filament winding RTM...

Product category：Fiberglass
Explain：
More details please refer to the products introductions
A：Fiberglass Stitched Mat
B：Single Warp Fiberglass Fabric
C：Fiberglass Stitch Bonded Fabric
D：Fiberglass Double Biaxial Fabric
E：Multiaxial core mat
F：Fiberglass Triaxial Fabric
G：Woven Roving Combo Mat

Product Examples

A：Fiberglass Stitched Mat

1.Features and usage:

Fiberglass stitched mat is made of chopped fiberglass strands in a certain length, then freely put and stitched together with polyester tissue or carbon fiber tissue by polyester yarn. It is compatible with Polyester, Vinyl and Epoxy resin and widely used in pultrusion pipes and tanks, FRP boat, insulation panels, anode tubes, auto parts, bath tubes etc, suitable for pultrusion, filament winding, RTM, hand lay-up processes.

2.General data

Code	Weight (g/m²)	Chopped strand (g/m²)	Polyester tissue (g/m²)	Carbon tissue (g/m²)	Moisture Content	Wet speed (≤S)
RUL250	250	250	-	-	≤0.2	≤60
RUL300	300	300	-	-	≤0.2	≤60
RUL300/C20	320	300	-	20	≤0.2	≤60
RUL300/N45	345	300	45	-	≤0.2	≤60
RUL380	380	380	-	-	≤0.2	≤60
RUL380/C20	400	380	-	20	≤0.2	≤60
RUL380/N45	425	380	45	-	≤0.2	≤60
RUL400	400	400	-	-	≤0.2	≤60
RUL400/C30	430	400	-	30	≤0.2	≤60
RUL400/N45	445	400	45	-	≤0.2	≤60
RUL450	450	450	-	-	≤0.2	≤60
RUL450/N45	495	495	45	-	≤0.2	≤60
RUL600	600	600	-	-	≤0.2	≤60

3.Remarks:

1) Roll width: Standard width in 1200mm, 1270mm, and other sizes depends on customer’s real needs, available in 200mm to 3200mm.
2) Packing: Fiberglass stitched mat is usually rolled in a paper tube with inner diameter 76mm. The roll is warped with plastic film, then put into carton. Lay the rolls horizontally, and can be loaded on pallets and bulk in container.
3) Storage: The product should be stored in a cool, water-proof area. It is recommended that the room temperature and humidity be always maintained at 15℃ to 35℃ and 35% to 65% respectively. Please keep the product in its original packaging before being used, avoiding moisture absorption.

B: Single Warp Fiberglass Fabric

1.Features and usage:

Single warp fiberglass fabric is made of fiberglass direct roving parallel aligned in 0°directions, then stitched by polyester yarn. Also can select to add chopped strand layer or non-woven fabric layer stitched together. It is compatible with Polyester, Vinyl and Epoxy resin and widely used in wind energy, boat building, FRP pipes and tanks, pultrusion section industry etc, suitable for pultrusion, hand lay up, filament winding, vacuum infusion processes.

2. General data

Code	Weight (g/m²)	0°Warp (g/m²)	90°Weft (g/m²)	Chop strands (g/m²)	Polyester tissue (g/m²)	Layer
RUL336	336	336	-	-	-	1
RUL400	400	400	-	-	-	1
RUL420	420	400	-	-	-	1
RUL560	560	560	-	-	-	1
RUL600	600	420	180	-	-	2
RUL625	625	400	-	225	-	2
RUL625/N45	670	400	-	225	45	3
RUL672	672	672	-	-	-	1
RUL800	800	672	128	-	-	2
RUL900	600	600	-	300	-	2

3. Remarks:

1) Roll width: Standard width in 1270mm, and other sizes depends on customer’s real needs, available in 200mm to 2600mm.
2) Packing: Single warp fiberglass fabric is usually rolled in a paper tube with inner diameter 76mm. The roll is warped with plastic film, then put into carton. Lay the rolls horizontally, and can be loaded on pallets and bulk in container.
3) Storage: The product should be stored in a cool, water-proof area. It is recommended that the room temperature and humidity be always maintained at 15℃ to 35℃ and 35% to 65% respectively. Please keep the product in its original packaging before being used, avoiding moisture absorption.

C: Fiberglass Stitch Bonded Fabric

1. Features and usage:

Fiberglass stitch bonded fabric is made of fiberglass direct roving parallel aligned in 0°and 90°directions, then stitched together with chopped strand layer or polyester tissue layer as combo mat. It is compatible with Polyester, Vinyl and Epoxy resin and widely used in boat building, wind energy, automotive, sports equipment, flat panels etc, suitable Vacuum infusion, hand lay-up, pultrusion, RTM forming processes.

2. General data

Code	Weight (g/m²)	0°Warp (g/m²)	90°Weft (g/m²)	Chop layer (g/m²)	Polyester tissue layer (g/m²)	Moisture content	Wet speed (≤S)
RUL400	400	224	176	-	-	≤0.2	≤60
RUL400/45	445	224	176	-	45	≤0.2	≤60
RUL-A-400/200	600	224	176	200	-	≤0.2	≤60
RUL-A-450/200	650	224	226	200	-	≤0.2	≤60
RUL600	600	336	264	-	-	≤0.2	≤60
RUL-B-600/45	645	336	264	-	45	≤0.2	≤60
RUL-A-600/300	900	336	264	300	-	≤0.2	≤60
RUL-A-600/450	1050	336	264	450	-	≤0.2	≤60
RUL800	800	420	380	-	-	≤0.2	≤60
RUL-B-800/45	845	420	380	-	45	≤0.2	≤60
RUL-A-800/250	1050	420	380	250	-	≤0.2	≤60
RUL-A-800/300	1100	420	380	300	-	≤0.2	≤60
RUL-A-800/450	1250	420	380	450	-	≤0.2	≤60
RUL1000	1000	560	440	-	-	≤0.2	≤60
RUL1200	1200	672	528	-	-	≤0.2	≤60
RUL-A-1200/300	1500	672	528	300	-	≤0.2	≤60

3. Remarks:

1) Roll width: Standard width in 1200mm, 1270mm, and other sizes depends on customer’s real needs, available in 200mm to 2600mm.
2) Packing: Fiberglass stitch bonded fabric is usually rolled in a paper tube with inner diameter 76mm. The roll is warped with plastic film, then put into carton. Lay the rolls horizontally, and can be loaded on pallets and bulk in container.
3) Storage: The product should be stored in a cool, water-proof area. It is recommended that the room temperature and humidity be always maintained at 15℃ to 35℃ and 35% to 65% respectively. Please keep the product in its original packaging before being used, avoiding moisture absorption.

D: Fiberglass Double Biaxial Fabric

1. Features and usage:
Fiberglass double biaxial fabric is made of fiberglass direct roving parallel aligned in +45°and -45°directions, then stitched together with or without chopped strand layer as combo mat. It is compatible with Polyester, Vinyl and Epoxy resin and widely used in boat building, wind energy, automotive, sports equipment, containers etc, suitable Vacuum infusion, hand lay-up, pultrusion, RTM forming processes.

2. General data

Code	Weight (g/m²)	+45°(g/m²)	-45°(g/m²)	Chop layer (g/m²)
RUL450	450	225	225	-
RUL600	600	300	300	-
RUL-A-600/225	825	300	300	225
RUL-A-600/300	900	300	300	300
RUL-A-600/450	1050	300	300	450
RUL800	800	400	400	-
RUL-A-800/225	1025	400	400	225
RUL-A-800/300	1100	400	400	300
RUL-A-800/450	1250	400	400	450

3. Remarks:

1) Roll width: Standard width in 1250mm, 1270mm, and other sizes depends on customer’s real needs, available in 200mm to2600mm.
2) Packing: Fiberglass double biaxial fabric is usually rolled in a paper tube with inner diameter 76mm. The roll is warped with plastic film, then put into carton. Lay the rolls horizontally, and can be loaded on pallets and bulk in container.
3) Storage: The product should be stored in a cool, water-proof area. It is recommended that the room temperature and humidity be always maintained at 15℃ to 35℃ and 35% to 65% respectively. Please keep the product in its original packaging before being used, avoiding moisture absorption.

E: Multiaxial core mat

1. Features and usage:

Multiaxial core mat is made of biaxial fabric (0°and 90°) combined middle layer PP, PET or Nylon core material and plus the chopped strands layer, then stitched together like sandwich design. It is compatible with Polyester, Vinyl and Epoxy resin and widely used in boat building, wind energy, automotive, train parts, storage tanks etc, suitable for RTM, Vacuum infusion, hand lay-up forming processes.

2. General data

Code	Weight (g/m²)	Biaxial layer (g/m²)	PP Core layer (g/m²)	Chop layer (g/m²)	Moisture content	Wet speed (≤S)
RULBA600/180/150	930	600	180	150	≤0.2	≤60
RULBA600/180/300	1080	600	180	300	≤0.2	≤60
RULBA600/180/600	1380	600	180	600	≤0.2	≤60
RULBA600/250/600	1450	600	250	600	≤0.2	≤60
RULBA800/250/300	1350	800	250	300	≤0.2	≤60
RULBA800/250/450	1500	800	250	450	≤0.2	≤60
RULBA800/250/600	1650	800	250	600	≤0.2	≤60

3. Remarks:

1) Roll width: Standard width in 1270mm, and other sizes depends on customer’s real needs, available in 200mm to 2600mm.
2) Packing: Fiberglass multiaxial core mat is usually rolled in a paper tube with inner diameter 76mm. The roll is warped with plastic film, then put into carton. Lay the rolls horizontally, and can be loaded on pallets and bulk in container.
3) Storage: The product should be stored in a cool, water-proof area. It is recommended that the room temperature and humidity be always maintained at 15℃ to 35℃ and 35% to 65% respectively. Please keep the product in its original packaging before being used, avoiding moisture absorption.

F: Fiberglass Triaxial Fabric

1. Features and usage:

Fiberglass triaxial fabric is made of fiberglass direct roving parallel aligned in 0°,+45°,-45°or +45°,90°,-45°directions, then stitched together with or without chopped strand layer as combo mat. It is compatible with Polyester, Vinyl and Epoxy resin and widely used in boat building, wind energy, automotive, sports equipment, containers etc, suitable Vacuum infusion, hand lay-up, pultrusion, RTM forming processes.

2. General data

Code	Weight (g/m²)	0° (g/m²)	+45°(g/m²)	90°(g/m²)	-45°(g/m²)	Chop layer (g/m²)
RULX600	600	300	150	-	150	-
RULX750	750	300	225	-	225	-
RULTX750	750	-	200	350	200	-
RULX900	900	300	300	-	300	-
RULTX900	900	-	225	450	225	-
RULX1200	1200	700	250	-	250	-
RULXA1200/300	1500	700	250	-	250	300
RULTXA1200/300	1500	-	250	700	250	300

3. Remarks:

1) Roll width: Standard width in1250mm, 1270mm, and other sizes depends on customer’s real needs, available in 200mm to2600mm.
2) Packing: Fiberglass triaxial fabric is usually rolled in a paper tube with inner diameter 76mm. The roll is warped with plastic film, then put into carton. Lay the rolls horizontally, and can be loaded on pallets and bulk in container.
3) Storage: The product should be stored in a cool, water-proof area. It is recommended that the room temperature and humidity be always maintained at 15℃ to 35℃ and 35% to 65% respectively. Please keep the product in its original packaging before being used, avoiding moisture absorption.

G: Woven Roving Combo Mat

1. Features and usage:
Woven roving combo mat is made of woven roving and chopped fiberglass strand complex of, then stitched together with polyester yarn. It is compatible with Polyester, Vinyl and Epoxy resin and widely used in boat building, Auto parts, refrigerated tools and structural sections industry etc, suitable for hand lay up, RTM, pultrusion, vacuum processes.

2. General data

Code	Weight (g/m²)	Woven roving (g/m²)	Chopped strand (g/m²)	Moisture Content	Wet speed (≤S)	Layer
RULRM200/200	400	200	200	≤0.2	60	2
RULRM300/300	600	300	300	≤0.2	60	2
RULRM400/300	700	400	300	≤0.2	60	2
RULRM500/300	800	500	300	≤0.2	60	2
RULRM500/450	950	500	450	≤0.2	60	2
RULRM600/300	900	600	300	≤0.2	60	2
RULRM600/450	1050	600	450	≤0.2	60	2
RULRM800/300	1100	800	300	≤0.2	60	2
RULRM800/450	1250	800	450	≤0.2	60	2

3. Remarks:

1) Roll width: Standard width in 1250mm, 1270mm, and other sizes depends on customer’s real needs, available in 200mm to 2600mm.
2) Packing: Fiberglass woven roving combo mat is usually rolled in a paper tube with inner diameter 76mm. The roll is warped with plastic film, then put into carton. Lay the rolls horizontally, and can be loaded on pallets and bulk in container.
3) Storage: The product should be stored in a cool, water-proof area. It is recommended that the room temperature and humidity be always maintained at 15℃ to 35℃ and 35% to 65% respectively. Please keep the product in its original packaging before being used, avoiding moisture absorption.