A: RC-670CWL、CML、CSL Unsaturated Polyester Resin
1. Features and usage:
RC-670CWL, RC-670CML, RC-670CSL are ortho-phthalic pre-accelerated unsaturated polyester resins, which have air-drying properties and are suitable for RTM injection molding process to manufacture general-purpose glass fiber reinforced plastics, waterproof boards and other products.
2. Technical index of liquid resin (25 ℃):
Item | Unit | RC-670CWL | RC-670CML | RC-670CSL | Testing Method |
Appearance | --- | light red transparent liquid | JIS K 6919.5.1. | ||
Viscosity | Pa·s | 0.20~0.28 | JIS K 6901.5.5. | ||
Gel Time | min | 6.0~10.0 | 8.0~12.0 | 12.0~16.0 | C83201 |
Note: Room temperature gel time: at 25℃, 2% MEKPO is added to the pot life (active oxygen is 9%), so that the injection period won’t be too short.
3. Physical properties of casting body (for reference only)
Item | Unit | Factual Value | Testing Method |
Tensile Strength | MPa | 65.2 | GB/T2567-2008 |
Elastic Tensile Modulus | GPa | 3.35 | GB/T2567-2008 |
Elongation at Break | --- | 3.42% | GB/T2567-2008 |
Bending Strength | MPa | 110 | GB/T2567-2008 |
Modulus of elasticity ( MOE) | GPa | 3.25 | GB/T2567-2008 |
Impact Strength | KJ/m2 | 14.0 | GB/T2567-2008 |
Heat Deflection Temperature | ℃ | 50 | GB/T1634-2004 |
Bacol hardness | --- | 39 | GB/T3854-2005 |
Note:
1) The manufacturing method of the casting body: GB/T8237-2005, the curing system: curing agent Butanox M-50 1.0%;
2) The post-treatment of the casting body: room temperature×24 hours+60℃×3 hours+80℃×1 hour.
4. Instructions
1) Butanox M-50 can be used as curing agent, and the dosage is 1.0-2.0%.
2) Cured after heating will make the products result a better performance.
5. Notices:
The product should be stored in a cool place below 25℃, avoid fire, and keep away from heat and radiation sources. The shelf life of storage below 25℃ is 3 months after leaving the factory.
6. Product Safety Data (SDS):
Before using this product, please read the SDS of this product in detail.
B:RC-1156 Unsaturated Polyester Resin
1. Features and usage:
RC-1156 is a moderately reactive ortho-phthalic pre-accelerated unsaturated polyester resin. It has low viscosity, high strength, good toughness, well permeant to glass fiber, and easy to demold. It is suitable for RTM process molding large-scale products such as wind power enclosures.
Summer type, suitable for June to August (above 25℃);
Spring and autumn type, suitable for March to May, September to October (15-25℃);
Winter type, suitable for 11-2 months (10-15℃).
2. Technical index of liquid resin (25 ℃):
Item | Unit | RC-H-1156S | RC-H-1156M | RC-H-1156W | Testing Method |
Viscosity | Pa·s | 0.15~0.19 | GB/T 7193.4.1 | ||
Gel Time | min | 85.0~110.0 | 60.0~85.0 | 35.0~60.0 | GB/T 7193.4.6 |
The range of gel time can be adjusted, curing system:curing agent Butanox M-50 1.5%.
3. Physical properties of casting body (for reference only)
Item | Unit | Factual Value | Testing Method |
Tensile Strength | MPa | 70 | GB/T2567-2008 |
Elastic Tensile Modulus | MPa | 3200 | GB/T2567-2008 |
Elongation at Break | --- | 4.5% | GB/T2567-2008 |
Bending Strength | MPa | 122 | GB/T2567-2008 |
Modulus of elasticity ( MOE) | MPa | 3300 | GB/T2567-2008 |
Heat Deflection Temperature | ℃ | 78 | GB/T1634-2004 |
Bacol hardness | --- | 46 | GB/T3854-2005 |
Note: 1) The sample method of the casting system: GB/T8237-2005. Curing system: Curing agent Butanox M-50 1.5% (addition can be adjusted appropriately according to actual needs)
2) Post-curing of the casting body: room temperature × 24 hours + 60°C × 3 hours + 85°C × 1 hour.
4. Instructions
1) Butanox M-50 can be used as curing agent, and the dosage is 1.0-2.0%.
2) Cured after heating will make the products result a better performance.
5. Notices:
The product should be stored in a cool place below 25℃, avoid fire, and keep away from heat and radiation sources. The shelf life of storage below 25℃ is 3 months after leaving the factory.
6. Product Safety Data (SDS):
Before using this product, please read the SDS of this product in detail.
C: RC-31029 Unsaturated Polyester Resin
1. Features and usage:
RC-31029 is a kind of ortho-phthalic unsaturated polyester resin. It has good wettability, high reactivity, fast curing, and excellent thermal strength. Products made with it are heat-resistant and have excellent mechanical properties, high modulus and high hardness, and are suitable for high-speed extrusion processes.
2. Technical index of liquid resin (25 ℃):
Item | Unit | Index | Testing Method |
Appearance | --- | Light yellow liquid | R6 |
Viscosity | Pa·s | 0.50~0.70 | RCI 18-021 |
SPI-GT | min | 4.0~6.0 | RCI 18-051 |
SPI -MCT | min | 1.2~2.3 | RCI 18-051 |
SPI -PET | ℃ | 226~260 | RCI 18-051 |
Acid Value | mgKOH/g | 14.0~19.0 | RCI 18-010 |
Non-volatile material | --- | (60.0~64.0)% | RCI 18-001 |
Note: gel time test: 50%BPO powder 2%
3. Physical properties of casting body (for reference only):
Item | Unit | Factual Value | Testing Method |
Tensile Strength | MPa | 40 | GB/T2567-2008 |
Elastic Tensile Modulus | MPa | 3100 | GB/T2567-2008 |
Elongation at Break | --- | 1.3% | GB/T2567-2008 |
Heat Deflection Temperature | ℃ | 105 | GB/T1634-2004 |
Bacol hardness | --- | 47 | GB/T3854-2005 |
Note:
1) The manufacturing method of the casting body: GB/T8237-2005, the curing system: RCA2.0%, Butanox M-50 1.0%;
2) The post-curing treatment of the casting body: room temperature×24 hours+60℃×3 hours+ 115℃×1 hour
4. Notices:
The product should be stored in a cool place below 25℃, avoid fire, and keep away from heat and radiation sources. The shelf life of storage below 25℃ is 3 months after leaving the factory.
5. Product Safety Data (SDS):
Before using this product, please read the SDS of this product in detail.
D: RC-130 Unsaturated Polyester Resin
1. Features and usage:
RC-130 is an ortho-phthalic unsaturated polyester resin. The product made of it has good rigidity and is not easy to deform. It is suitable for extrusion and manufacturing of fishing poles, tent poles, grilles and other products.
2. Technical index of liquid resin (25 ℃):
Item | Uniform | Index | Testing Method |
Gardner | --- | below 2 | JIS K 6901.5.2 |
Viscosity | Pa·s | 0.35~0.55 | JIS K 6901.5.5.1 |
Gel Time | min | 7.0~10.0 | JIS K 6901.5.10 |
Note: gel time test: RC 2% M (input) 2%
3. Physical properties of casting body (for reference only)
Item | Uniform | Index | Testing Method |
Tensile Strength | MPa | 50 | GB/T2567-2008 |
Elastic Tensile Modulus | MPa | 3700 | GB/T2567-2008 |
Elongation at Break | --- | 1.3% | GB/T2567-2008 |
Bending Strength | MPa | 110 | GB/T2567-2008 |
Modulus of elasticity ( MOE) | MPa | 4220 | GB/T2567-2008 |
Heat Deflection Temperature | ℃ | 90 | GB/T1634-2004 |
Note:
1) The manufacturing method of casting body: GB/T8237-2005, curing system: accelerator RCA 1.0%, curing agent Butanox M-50 1.0%;
2) Post-treatment of casting body: room temperature×24 hours+60℃×3 Hour+100℃×1 hour.
4. Notices:
The product should be stored in a cool place below 25℃, avoid fire, and keep away from heat and radiation sources. The shelf life of storage below 25℃ is 3 months after leaving the factory.
5. Product Safety Data (SDS):
Before using this product, please read the SDS of this product in detail.
E: RC-R-1001 Unsaturated Polyester Resin
1. Features and usage:
RC-R-1001 resin is an ortho-phthalic unsaturated polyester resin. FRP products made of it reinforced plastic products have good mechanical strength and high elongation, and have strong versatility, and are suitable for making glass fiber reinforced plastic products by pultrusion.
2. Technical index of liquid resin (25 ℃):
Item | Uniform | Index | Testing Method |
Appearance | --- | Light yellow transparent liquid | GB/T8237.6.1.1 |
Viscosity | Pa·s | 0.30~0.45 | GB/T7193.4.1 |
Gel Time | min. | 9.1~16.9 | GB/T7193.4.6 |
Non-volatile material | --- | (61.0~67.0)% | GB/T7193.4.3 |
Note: Gel time test: resin 50g RCA: 1.5g M-50: 1.0g
3. Physical properties of casting body (for reference only
Item | Uniform | Index | Testing Method |
Tensile Strength | MPa | 65 | GB/T2567-2008 |
Elongation at Break | --- | 3.7% | GB/T2567-2008 |
Bending Strength | MPa | 112 | GB/T2567-2008 |
Impact Strength | KJ/m2 | 10.3 | GB/T2567-2008 |
Heat Deflection Temperature | ℃ | 70 | GB/T1634-2004 |
Bacol hardness | --- | 42 | GB/T3854-2005 |
Note:
1) The casting system sample method: GB/T8237-2005, the curing system: accelerator RCA 1.0%, curing agent Butanox M-50 1.0%;
2) Post-curing treatment of the cast body: room temperature × 24 hours + 60° C. × 3 hours + 80° C. × 1 hour.
4. Notices:
The product should be stored in a cool place below 25℃, avoid fire, and keep away from heat and radiation sources. The shelf life of storage below 25℃ is 3 months after leaving the factory.
5. Product Safety Data (SDS):
Before using this product, please read the SDS of this product in detail.
TEL:86-13814790407 QQ:2314301513
Copyright © Changzhou Rule Composite Material Co., Ltd, | keep on record:苏ICP备2021025817号-1
Address:No. 601, No.16 Taihu Middle Road, Xinbei District, Changzhou City Jiangsu Province,China